Rapid manufacture of sodium polyaluminate electrolyte ceramics for solid state batteries via direct ink writing

Solid-state electrolyte structures using sodium polyaluminate ceramics, have been fabricated for the first time using direct ink writing; a material extrusion-based additive manufacturing process. A series of test samples were prepared using a high solids loading (80 wt%; 51.2 vol%) ceramic paste formulations with suitable rheological characteristics for 3D printing. Following optimum densification via conventional sintering at 1600 °C for 30 min, the additively manufactured electrolyte test samples exhibited an ionic conductivity of σ = 0.14 ± 0.019 S·cm−1 at 300 °C and density of ρ = 3.1 ± 0.02 g·cm−3 (relative density of 95%). These results suggest that direct ink writing of sodium polyaluminates is a promising approach for electrolyte manufacture. Additionally, this approach shows great potential for manufacturing complete solid-state battery structures, through multi-material direct ink writing.