Tunable Crosslinking, Reversible Phase Transition, and 3D Printing of Hyaluronic Acid Hydrogels via Dynamic Coordination of Innate Carboxyl Groups and Metallic Ions

This article reports tunable crosslinking, reversible phase transition, and three-dimensional printing (3DP) of hyaluronic acid (HyA) hydrogels via dynamic coordination of Fe³⁺ ions with their innate carboxyl groups for the first time. The concentrations of Fe³⁺ and H⁺ ions and the reaction time determine the tunable ratios of mono-, bi-, and tridentate coordination, leading to the low-to-high crosslinking densities and reversible solid–liquid phase transition of HyA hydrogels. At the monodentate-dominant coordination, the liquid hydrogels have low crosslinking densities (HyA_L). At the mixed coordination of mono-, bi-, and tridentate bonding, the solid hydrogels have medium crosslinking densities (HyA_M). At the tridentate-dominant coordination, the solid hydrogels have high crosslinking densities (HyA_H). The reversible solid–liquid phase transitions among HyA_L, HyA_M, and HyA_H were achieved via controlling the concentrations of Fe³⁺ and H⁺ ions and reaction time. When the crosslinking densities are between HyA_L and HyA_M, the hydrogels become 3D printable (HyA_P). HyA_P hydrogels were 3D-printed successfully using cold-stage or direct writing methods, and the 3D constructs achieved better structural stability using the latter method. In the direct exposure culture with bone marrow-derived mesenchymal stem cells, the 3D-printed HyA_H (HyA_H_3D) and HyA_H hydrogels showed higher average cell adhesion densities than the HyA_M, HyA_P, and HyA_L hydrogel groups under both direct and indirect contact conditions. For all hydrogel groups, cell adhesion densities under direct contact conditions were statistically lower than the same groups under indirect contact conditions. In this article, we elucidated the mechanisms of dynamic coordination and the relationships among the key parameters in controlling the tunable crosslinking, reversible phase transition, and 3DP of HyA hydrogels without blending with other polymers or adding functional groups. This approach can be potentially adapted to crosslink and 3D print other polymeric hydrogels with carboxyl groups, which is promising for a wide range of applications.