Conductive Composite Fibres from Reduced Graphene Oxide and Polypyrrole Nanoparticles
Continuous composite fibres composed of polypyrrole (PPy) nanoparticles and reduced graphene oxide (rGO) at different mass ratios were fabricated using a single step wet-spinning approach. The electrical conductivity of the composite fibres increased significantly with the addition of rGO. The mechanical properties of the composite fibres also improved by the addition of rGO sheets compared to fibres containing only PPy. The ultimate tensile strength of the fibres increased with the proportion of rGO mass present. The elongation at break was greatest for the composite fibre containing equal mass ratios of PPy nanoparticles and rGO sheets. L929 fibroblasts seeded onto fibres…
Functional 3D Neural Mini-Tissues from Printed Gel-Based Bioink and Human Neural Stem Cells
Direct-write printing of stem cells within biomaterials presents an opportunity to engineer tissue for in vitro modeling and regenerative medicine. Here, a first example of constructing neural tissue by printing human neural stem cells that are differentiated in situ to functional neurons and supporting neuroglia is reported. The supporting biomaterial incorporates a novel clinically relevant polysaccharide-based bioink comprising alginate, carboxymethyl-chitosan, and agarose. The printed bioink rapidly gels by stable cross-linking to form a porous 3D scaffold encapsulating stem cells for in situ expansion and differentiation. Differentiated neurons form synaptic contacts, establish networks, are spontaneously active, show a bicuculline-induced increased calcium…
From nanoparticles to fibres: effect of dispersion composition on fibre properties
A polyvinyl alcohol (PVA)-stabilized polypyrrole nanodispersion has been optimised for conductivity and processability by decreasing the quantity of PVA before and after synthesis. A reduction of PVA before synthesis leads to the formation of particles with a slight increase in dry particle diameter (51 ± 6 to 63 ± 3 nm), and conversely a reduced hydrodynamic diameter. Conductivity of the dried nanoparticle films was not measureable after a reduction of PVA prior to synthesis. Using filtration of particles after synthesis, PVA content was sufficiently reduced to achieve dried thin film conductivity of 2 S cm−1, while the electroactivity of the…