Rapid bone regeneration in implants is important for successful transplantation. In this regard, we report the development of calcium silicate/zinc silicate (CS/ZS) dual-compound-incorporated calcium phosphate cement (CPC) scaffolds with a three-dimensional poly (lactic-co-glycolic acid) network that synergistically promote bone regeneration. In vitro results demonstrated that the incorporation of CS/ZS dual compounds into the CPC significantly promoted the osteogenic differentiation of stem cells compared to the addition of CS or ZS alone. Moreover, the bone-regeneration efficacy of the composite scaffolds was validated by filling in femur condyle defects in rabbits, which showed that the scaffolds with CS and ZS possessed a…

Creating interconnected macropores in calcium phosphate cement (CPC) is an effective strategy to promote its degradation and osteogenesis. However, little attention has been given to the osteogenic effect of the CPC scaffolds with pre-forming and in-situ forming interconnected macropores. Herein, two types of CPC scaffolds were prepared by infiltrating CPC pastes into 3D-printed polycaprolactone (PCL) and poly(lactic-co-glycolic acid) (PLGA) networks. Meanwhile, the sacrificial PCL network within CPC was dissolved to obtain the CPC scaffold with approximately 300 μm macropores, whereas the PLGA network was retained within the CPC to obtain the PLGA/CPC scaffold. The results indicated that the PLGA/CPC scaffold…

Calcium phosphate cement (CPC) is widely used in orthopedics, dentistry and spine surgery because of its excellent biocompatibility, osteoconductivity, arbitrary shaping and self-setting ability. However, slow degradation rate of CPC decreases its bone regeneration efficacy. Herein, poly (lactic co-glycolic acid) microspheres (PLGAm) and wollastonite (WS) were mixed with CPC powder to prepare CPC composite pastes, and then the composite pastes were perfused into poly (lactic co-glycolic acid) network (PLGAnw) to construct composite bone repair materials. The degradation of PLGAnw generated interconnected macropores with the short side of about 468 μm along horizontal axis and the long side of about 785…