3D Bioplotter Research Papers

Objectives There are complications in applying regenerative strategies at the interface of hard and soft tissues due to the limited designs of constructs that can accommodate different cell types in different sites. The problem originates from the challenges in the adhesion of dissimilar materials, such as polymers and hydrogels, that can be suitable for regenerating different tissues such as bone and soft tissues. This paper presents a design of a new hybrid construct in which a polymer (polycaprolactone (PCL)) membrane firmly adheres to a layer of hydrogen (gelatin). Methods PCL membranes with defined size and porosity were fabricated using 3D…

A modular design composed of 3D-printed polycaprolactone (PCL) as the load-bearing module, and dual porosity gelatin foam as the bio-reactive module, was developed and characterized in this study. Surface treatment of the PCL module through aminolysis-aldehyde process was found to yield a stronger interface bonding compared to NaOH hydrolysis, and therefore was used in the fabrication procedure. The modular scaffold was shown to significantly improve the mechanical properties of the gelatin foam. Both compressive modulus and ultimate strength was found to increase over 10 times when the modular design was employed. The bio-reactive module i.e., gelatin foam, presented a dual…

Pressure-assisted coating (PAC) is introduced to coat 3D-printed polymeric scaffolds with β-tricalcium phosphate (β-TCP) for tissue engineering applications. The method consists of four steps: infiltration of ceramic particles into the porous structure of the polymeric scaffold, dehydration of the slurry, compaction of ceramic particles around the scaffold, and heat treatment. The optimal coating is obtained at an infiltration speed of 400 mm/min followed by complete dehydration, compaction under ca. 8 MPa pressure, and subsequent heat treatment at 65 °C. The outcome is a uniformly coated scaffold with no deformation or structural defects, as confirmed by micro-CT analysis and laser and…

Improving bone regeneration is one of the most pressing problems facing bone tissue engineering (BTE) which can be tackled by incorporating different biomaterials into the fabrication of the scaffolds. The present study aims to apply the 3D-printing and freeze-drying methods to design an ideal scaffold for improving the osteogenic capacity of Dental pulp stem cells (DPSCs). To achieve this purpose, hybrid constructs consisted of 3D-printed Beta-tricalcium phosphate (β-TCP)-based scaffolds filled with freeze-dried gelatin/reduced graphene oxide-Magnesium-Arginine (GRMA) matrix were fabricated through a novel green method. The effect of different concentrations of Reduced graphene oxide-Magnesium-Arginine (RMA) (0, 0.25% and 0.75%wt) on the…

Porous scaffolds were 3D-printed using poly lactic-co-glycolic acid (PLGA)/TiO2 composite (10:1 weight ratio) for bone tissue engineering applications. Addition of TiO2 nanoparticles improved the compressive modulus of scaffolds. Differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) revealed an increase in both glass transition temperature and thermal decomposition onset of the composite compared to pure PLGA. Furthermore, addition of TiO2 was found to enhance the wettability of the surface evidenced by reducing the contact angle from 90.5 ± 3.2 to 79.8 ± 2.4 which is in favor of cellular attachment and activity. The obtained results revealed that PLGA/TiO2 scaffolds significantly improved osteoblast proliferation compared to…